SMALL BATCH PRODUCTION
MJF 3D PRINTING SERVICE
We run 2 HP Jet Fusion 4200 Industrial 3D Printers
Industrial Grade 3D Printers
HP Multi Jet Fusion uses a fine-grained PA 12 material that allows for ultra-thin layers of 80 microns. This leads to parts with high density and low porosity, compared to PA 12 parts produced with Laser Sintering. It also leads to an exceptionally smooth surface straight out of the printer, and functional parts need minimal post-production finishing.
GET IN TOUCH TODAY
+44 (0) 1474 550 934
Engineering-grade material optimized for 3D printing efficiency
ADDITIVE 3D PRINTING TECHNOLOGY
FOR A WIDE RANGE OF APPLICATIONS FIELDS
-
Design
-
Architecture
-
Automotive
-
Aerospace
-
Engineering
-
Biomedical
-
Heritage
We are able to 3D print hundred
of protoypes quickly and cost effectively
NYLON PA12
MATERIAL
-
Density of parts:
1.01 g/cm3 -
Tensile Strength, Max Load - XY: 48 MPa/6960 psi
-
Tensile Strength, Max Load - Z: 48 MPa/6960 psi
-
Tensile Modulus4 - XY: 1700 MPa/245 ksi
-
Tensile Modulus4 - Z:
1800 MPa/260 ksi -
Max. part Dimension:
256 x 340 x 360 mm -
Elongation at Break4 - XY: 20%
-
Elongation at Break4 - Z structure: 15%
-
Heat Deflection Temperature - Z:
175°C @ 0.45 MP
95°C @ 1.82 MPa
Standard:
ASTM D792, ASTM D638 ASTM D648
TECHNICAL
SPECIFICATIONS
-
Dimensional accuracy: ±0.3 mm
-
Layer thickness: 0.08 mm
-
Min. thickness: 0.25 mm
-
Min. detail: 0.25 mm
-
Min. clearance: 0.4~0.5mm
-
Max. part Dimension:
-
256 x 340 x 360 mm
-
Post finishing: yes
-
Surface
-
structure: Unfinished parts typically have a smooth surface, without visible layers, and a stone-grey color. Multi Jet Fusion parts can be sandblasted and dyed